Product Description TraSys® 414 heavy-duty mold release coating is a translucent water-based dispersion for rotational molding applications. When applied to a mold, it exhibits outstanding release or antistick properties and has a very low coefficient of friction. It is clean, nonoily, nonstaining, chemically inert, and can function in temperatures to 260°C (500°F) or higher. TraSys® 414 will meet molders’ production, environmental, and safety requirements. It offers an unmatched combination of lubricity and durability, without the use of silicone oils, providing consistent release and reducing mold buildup. TraSys® 414 is solvent-free, meeting all existing and anticipated environmental regulations. Additionally, TraSys® 414 contains no alcohols that may form flammable vapors. Uses TraSys® 414 heavy-duty release is ideal for rotational mold parting lines and removable pins and inserts or cores and projecting areas that molded plastic forms around and causes difficulty in demolding. Direction for Use TraSys® 414 must be agitated before use. TraSys® 414 mold release coating should be applied to clean and dry surfaces. For maximum results, preheat the mold surface to 55–60°C (130–140°F) before application.

Recommended Procedure 1. Clean mold thoroughly, using glass or plastic bead media, abrasive pads, and cleaning solvent or high pH detergent, to remove all prior mold release and other sources of contamination. 2. If spraying, use spray equipment that provides a fine mist. When wiping, lightly dampen a clean cloth with TraSys® 414 after agitation. After agitation, apply lightly to the mold’s surfaces, making certain that all areas of the mold are entirely coated. 3. A minimum inner mold temperature of 132°C (270°F) is recommended to cure the release. This can easily be accomplished after application by running the mold empty through a full production cycle with the oven temperature at 170°C (350°F). Proper curing will give a bond between mold and coating that will ensure no transfer of coating to the first molded part, as well as ensure the most effective coating for durability and cycle life. 4. When spot touch-ups are applied, curing the freshly coated area with a heat gun will further enhance the bond between the coating and the mold’s surface. Larger applications may require a bake cycle as described above

产品描述
TraSys®414重型脱模涂料是一种半透明水基分散体用于滚塑成型应用。当应用于模具时，它具有出色的脱模性或抗粘性
并且具有非常低的摩擦系数。它是透明的，非油性，无污染，化学惰性，可以在260°C（500°F）或更高的温度下工作。
TraSys®414将满足模塑商的生产，环境和安全要求。它提供了一个无与伦比的润滑性和耐用性，不使用硅油，提供一致性脱模并减少霉菌堆积。 TraSys®414是无溶剂，符合所有现有和预期的
环境法规。此外，TraSys®414不含可能形成易燃蒸气的醇类。
用途
TraSys®414重载释放装置是旋转的理想选择模具分型线和可拆卸的销和插件或塑料成型的型芯和突出区域周围并导致脱模困难。
使用指南
使用前必须搅拌TraSys®414。 TraSys®414脱模涂料应适用于清洁和干燥的表面。为获得最佳效果，请预热模具施工前表面温度为55-60°C（130-140°F）。

推荐程序
1.使用玻璃或塑料珠彻底清洁模具介质，研磨垫和清洁溶剂或高pH洗涤剂，去除所有先前的脱模剂和其他污染源。
2.如果喷涂，请使用提供的喷涂设备细雾。擦拭时，轻轻蘸一块干净的布搅拌后用TraSys®414。搅拌后，轻轻涂抹在模具表面，确定模具的所有区域都是完全涂层的。
3.最低内模温度为132°C（270°F）建议固化释放。这个申请后可以轻松完成通过全面生产将模具清空烘箱温170°C（350°F）时循环。适当的固化会在模具和模具之间产生粘合涂层，确保涂层不会转移第一个模塑部件，以及最大的保证有效涂层，耐用性和循环寿命。
4.当应用点修饰时，固化带有热风枪的新涂层区域将进一步增加增强涂层与涂层之间的粘合模具表面。较大的应用程序可能需要如上所述的烘烤循环