Product Description

TraSys® 500 mold release coating is a translucent water-based dispersion for high heat and open ame rotational molding applications. When applied to a mold, it exhibits outstanding release or antistick prop- erties and has a very low coef cient of friction. It is clean, nonoily, nonstaining, chemically inert, and can function in temperatures to 315°C (600°F) or higher.

TraSys® 500 will meet molders’ production, environmental, and safety requirements. It offers an unmatched combination of lubricity and durability, without the use of silicone oils, providing consistent release and reducing mold buildup. TraSys® 500 is solvent-free, meeting all existing and anticipated envi- ronmental regulations. Additionally, TraSys® 500 con- tains no alcohols that may form ammable vapors.

Uses

TraSys® 500 is ideal for rotational mold internals and other molding applications where a consistent, controlled release is desired.

Direction for Use

TraSys® 500 must be agitated before use. TraSys® 500 mold release coating should be applied to clean and dry surfaces. For maximum results, preheat the mold surface to 55–60°C (130–140°F) before application.

Recommended Procedure

1. Clean mold thoroughly, using glass or plastic bead media, abrasive pads, and cleaning solvent or high pH detergent, to remove all prior mold release and other sources of contamination.

2. If spraying, use spray equipment that provides a ne mist. When wiping, lightly dampen a clean cloth with TraSys® 500 after agitation. After agitation, apply lightly to the mold’s surfaces, making certain that all areas of the mold are entirely coated.

3. A minimum inner mold temperature of 132°C (270°F) is recommended to cure the release. This can easily be accomplished after application by running the mold empty through a full production cycle with the oven temperature at 170°C (350°F). Proper curing will give a bond between mold and coating that will ensure no transfer of coating to the rst molded part, as well as ensure the most effective coating for durability and cycle life.

4. When spot touch-ups are applied, curing the freshly coated area with a heat gun will further enhance the bond between the coating and the mold’s surface. Larger applications may require a bake cycle as described above.

Typical Properties

Primary Polymer: Fluorochemical

Specific Gravity: 1.0

Odor:
 Slight

Color: White

Flash Point: None

Storage and Handling

TraSys® 500 should be stored in a cool, dry, well ventilated area. Do not expose to freezing tempera- tures. Freezing will affect the physical condition, but will not damage the release effectiveness. Thaw at room temperature, and mix well before using.

Containers in use should be agitated before use and often during use. Drums will require a low rpm agitator to prevent phase separation in the storage container.

Breathing vapors should be avoided. If spraying, care should be taken to avoid inhaling mist or vapors, just as sprayed paint inhalation should be avoided.

Care should be taken not to expose TraSys® 500 mold release coating to open ame or intense heat. Temper- atures above 315°C (600°F) may cause chemical break- down, resulting in toxic fumes. Always wash hands after handling TraSys® 500 mold release coating.

Shelf Life

TraSys® 500 has a shelf life of 1 year from the date of shipment.

Packaging

TraSys® 500 is available in 1-, 5-, and 55-gal containers. Larger volume orders may be packaged in specialty containers.

Shipping Limitations

None

产品描述

TraSys®500脱模涂料是一种半透明的水基分散体，适用于高热量和开放式阿姆斯旋转成型应用。当应用于模具时，它具有出色的释放性或抗粘性，摩擦系数非常低。它干净无暇，无污染，化学惰性，可在温度达到315°C（600°F）或更高温度时起作用。

TraSys®500将满足模塑商的生产，环境和安全要求。它提供了无与伦比的润滑性和耐久性组合，无需使用硅油，从而提供一致的释放并减少模具积聚。 TraSys®500无溶剂，符合所有现有和预期的环境法规。另外，TraSys®500不含可能形成易燃蒸气的醇类。

用途

TraSys®500是理想的旋转模具内部件和其他需要一致控制释放的成型应用。

使用指南

使用前必须搅拌TraSys®500。 TraSys®500脱模剂涂层应用于清洁和干燥的表面。为获得最佳效果，在使用前将模具表面预热至55-60°C（130-140°F）。

推荐程序

1.使用玻璃或塑料珠介质，研磨垫，清洁溶剂或高pH值清洁剂彻底清洁模具，以去除所有之前的脱模剂和其他污染源。

2.如果喷涂，使用喷雾设备，以提供雾气。擦拭时，请在搅拌后用TraSys®500轻轻擦拭干净的布。搅动后，轻轻涂抹模具表面，确保模具的所有区域均完全涂覆。

3.建议使用132℃（270°F）的最低内模温度来固化释放。通过在烘箱温度为170°C（350°F）的整个生产周期中将模具放空，可以很容易地完成该操作。适当的固化会在模具和涂层之间形成粘合，从而确保涂层不会转移到第一个模制部件上，并确保最有效的涂层提供耐用性和循环寿命。

4.当进行点接触时，用热风枪固化新涂层区域将进一步增强涂层与模具表面之间的结合。如上所述，较大的应用可能需要烘烤周期。

典型属性

主要聚合物：含氟化合物

比重：1.0

气味：轻微

白颜色

闪点：无

存储和处理

TraSys®500应储存在阴凉，干燥，通风良好的地方。不要暴露在寒冷的气温下。冷冻会影响身体状况，但不会损害释放效果。在室温下解冻，并在使用前充分混合。

使用中的容器应在使用前经常搅动，并经常在使用过程中。鼓将需要低转速的搅拌器以防止储存容器中的相分离。

应避免呼吸蒸气。如果进行喷涂，应注意避免吸入雾气或蒸气，正如应避免喷涂喷漆一样。

应注意不要让TraSys®500脱模涂层暴露在光亮或高温下。高于315°C（600°F）的温度可能会导致化学物质分解，导致有毒烟雾。处理TraSys®500脱模涂层后请务必洗手。

保质期

TraSys®500自发货之日起保质期为1年。

打包

TraSys®500有1个，5个和55加仑的容器可供选择。大批量订单可能包装在专用容器中。

运输限制

没有